| Grade : | 1.4002耐腐蝕鋼片/板和帶材 | |||||
| Number: | X6CrAl13 | |||||
| Classification: | 鐵素體不銹鋼 | |||||
| Density: | 7.7 g/cm 3 | |||||
| Standard: | ||||||
| EN 10088-2:2005不銹鋼。通用耐腐蝕鋼片/板和帶材交貨技術(shù)條件 | ||||||
| EN 10250-4:2000一般工程用開(kāi)口鋼模鍛件。不銹鋼 | ||||||
| EN 10297-2:2005機(jī)械和一般工程用無(wú)縫圓形鋼管。不銹鋼。技術(shù)交付條件 | ||||||
| EN 10088-1:2005不銹鋼。不銹鋼清單 | ||||||
| Equivalent grades: | ||||||
| Chemical comb % of steel X6CrAl13 (1.4002): EN 10088-2-2005 | ||||||
| 未經(jīng)買方同意，不得故意將本表中未列出的元素添加到鋼材中，除非對(duì)鑄件進(jìn)行精加工。 | ||||||
| 硫含量的特定范圍可以提供特定性能的改善。對(duì)于可加工性，建議并允許將硫含量控制在0.015%至0.030%之間。對(duì)于可焊性，建議并允許將硫含量控制在0.008%至0.030%之間。對(duì)于可極化性，建議將硫含量控制在最大0.015%。 | ||||||
| C | Si | Mn | P | S | Cr | Al |
| max 0.08 | max 1 | max 1 | max 0.04 | max 0.015 | 12月14日 | 0.1 - 0.3 |
| Mechanical properties of steel X6CrAl13 (1.4002) | ||||||
| Rm - Tensile strength (MPa) (+A) | 400-600 | |||||
| Rp0.2 0.2% proof strength (MPa) (+A) | 210-230 | |||||
| A - Min. elongation at fracture (%) (+A) | 17 |