| Grade : | Z7CN18-09彈簧用不銹鋼帶 | ||||||
| Number: | X5CrNi18-10 | ||||||
| Classification: | 奧氏體不銹鋼 | ||||||
| Density: | 7.9 g/cm 3 | ||||||
| Standard: | |||||||
| EN 10088-2:2005不銹鋼。通用耐腐蝕鋼片/板和帶材交貨技術(shù)條件 | |||||||
| EN 10088-3:2005不銹鋼。一般用途耐腐蝕鋼的半成品、棒材、線材、型材和光亮產(chǎn)品的交貨技術(shù)條件 | |||||||
| EN 10028-7:2007壓力用鋼制扁平產(chǎn)品。不銹鋼 | |||||||
| EN 10222-5:2000壓力用鋼鍛件。馬氏體、奧氏體和奧氏體-鐵素體不銹鋼 | |||||||
| EN 10151:2003彈簧用不銹鋼帶。技術(shù)交付條件 | |||||||
| EN 10216-5:2014壓力用無(wú)縫鋼管。技術(shù)交付條件。不銹鋼管 | |||||||
| EN 10217-7:2005壓力用焊接鋼管。不銹鋼管 | |||||||
| EN 10296-2:2005機(jī)械和一般工程用焊接圓鋼管。不銹鋼。技術(shù)交付條件 | |||||||
| EN 10253-3:2008對(duì)焊管件。無(wú)特殊檢驗(yàn)要求的鍛造奧氏體和奧氏體-鐵素體（雙相）不銹鋼 | |||||||
| EN 10253-4:2008對(duì)焊管件。有特殊檢驗(yàn)要求的鍛制奧氏體和奧氏體-鐵素體（雙相）不銹鋼 | |||||||
| EN 10269:1999具有規(guī)定高溫和/或低溫性能的緊固件用鋼和鎳合金 | |||||||
| EN 10272:2007壓力用不銹鋼棒 | |||||||
| EN 10263-5:2001冷鐓和冷擠壓用鋼條、棒材和線材。不銹鋼交貨技術(shù)條件 | |||||||
| EN 10250-4:2000一般工程用開口鋼模鍛件。不銹鋼 | |||||||
| EN 10297-2:2005機(jī)械和一般工程用無(wú)縫圓形鋼管。不銹鋼。技術(shù)交付條件 | |||||||
| EN 10088-4:2009不銹鋼。建筑用耐腐蝕鋼片/板和帶材交貨技術(shù)條件 | |||||||
| EN 10088-5:2009不銹鋼。建筑用耐腐蝕鋼棒材、棒材、線材、型材和光亮產(chǎn)品的交貨技術(shù)條件 | |||||||
| Equivalent grades: | |||||||
| Chemical comb % of steel X5CrNi18-10 (Z7CN18-09): EN 10088-2-2005 | |||||||
| 硫含量的特定范圍可以提供特定性能的改善。對(duì)于可加工性，建議并允許將硫含量控制在0.015%至0.030%之間。對(duì)于可焊性，建議并允許將硫含量控制在0.008%至0.030%之間。對(duì)于可極化性，建議將硫含量控制在最大0.015%。 | |||||||
| 未經(jīng)買方同意，不得故意將本表中未列出的元素添加到鋼材中，除非對(duì)鑄件進(jìn)行精加工。 | |||||||
| C | Si | Mn | Ni | P | S | Cr | N |
| max 0.07 | max 1 | max 2 | 8 - 10.5 | max 0.045 | max 0.015 | 17.5 - 19.5 | max 0.11 |
| Mechanical properties of steel X5CrNi18-10 (Z7CN18-09) | |||||||
| Rm - Tensile strength (MPa) (+A) | 500-750 | ||||||
| Rm - Tensile strength (MPa) (+AT) | 500-700 | ||||||
| Rm - Tensile strength (MPa) (+AT+C) | 780-820 | ||||||
| Rp0.2 0.2% proof strength (MPa) (+AT) | 195 | ||||||
| Rp0.2 0.2% proof strength (MPa) (+A) | 190-235 | ||||||
| KV - Impact energy (J) transverse, (+A) | +20° | -196° | |||||
| 60 | 60 | ||||||
| KV - Impact energy (J) longitud., (+A) | +20° | ||||||
| 100 | |||||||
| A - Min. elongation at fracture (%) (+A) | 35-45 | ||||||
| A - Min. elongation at fracture (%) longitud., (+AT) | 40 | ||||||
| Vickers hardness ( HV): (+CR) | 220 - 450 | ||||||
| Brinell hardness (HB): (+A) | 215 | ||||||
| Brinell hardness (HB): (+AT) | 200 | ||||||