| PMMA DR101 法國阿托菲納公司 物性數(shù)據(jù) |
| 規(guī)格級別： | --- | 外觀顏色： | --- |
| 用途概述： | --- | ||
| 備注說明： | 高抗沖擊 | ||
| 性能項目 | 試驗條件[狀態(tài)] | 測試方法 | 測試數(shù)據(jù) | 數(shù)據(jù)單位 | |
| 基本性能 | 熔體流動速率 | --- | ASTM D-1238 | 1.0 | g/10min |
| 吸水率 | 浸水24hrs后增重 | ASTM D-570 | 0.4 | % | |
| 物理性能 | 透光率 | --- | ASTM D-1003 | 91 | % |
| 折射率ND | --- | ASTM D-542 | 1.49 | --- | |
| 比重 | --- | ASTM D-792 | 1.15 | --- | |
| 霧度 | --- | --- | <3 | % | |
| 成形收縮率 | (冷模/冷件),48hrs | ASTM D-935 | 0.3-0.8 | % | |
| 機械性能 | 彎曲模數(shù) | --- | ASTM D-790 | 19000 | kgf/cm2 |
| 沖擊強度 | Izod研磨缺口 | ASTM D-256 | 5.9(57.9) | kgf.cm/cm(J/m) | |
| 沖擊強度 | 落錘(15.2×15.2×0.3cm重1.4kg半徑0.64cm) | ASTM D-256 | 136(14) | kg.cm(J) | |
| 洛氏硬度 | --- | ASTM D-758 | 45 | M scale | |
| 拉伸強度 | 初級應(yīng)變速率0.1cm/cm/min | ASTM D-638 | 390(38) | kgf/cm2 | |
| 彎曲強度 | 橫跨比=16 | ASTM D-790 | 720(71) | kgf/cm2(MPa) | |
| 熱 性 能 | 熱變形溫度負(fù)荷 | 退火2℃/min,18.6kgf/cm2 | ASTM D-648 | 79 | ℃ |
| 使用溫度范圍 | 與殘余應(yīng)力大小有關(guān) | --- | 71-82 | ℃ | |
| 維卡軟化點 | 未退火,50℃/hr,1kg | ASTM D-1525 | 98 | ℃ | |
| 維卡軟化點 | 未退火,50℃/hr,5kg | ASTM D-1525 | 86 | ℃ | |